What is the difference between 6005 and 6005A?
The main difference between the two alloys is that 6005 has a higher minimum composition percentage of aluminium than 6005A (while having essentially the same maximum). The most common forming method is extrusion. It can also be forged or rolled, but as a wrought alloy it is not used in casting.
What is the difference between 6005 and 6061?
Alloy 6005 is similar to alloy 6061. When produced to a -T5 temper, it has the same minimum tensile and yield strength as 6061-T6 and better machinability and strength properties than 6063-T6. Alloy 6005A may also replace 6061 due to its better extrudability and surface appearance.
What is AlSi10Mg?
EOS Aluminium AlSi10Mg is a widely used alloy that combines light weight and good mechanical properties. Different heat treatments can be applied to modify properties for example to increase ductility and conductivity. The material has good thermal and electrical conductivity especially after heat treatment.
What is AL6005 T5?
Product Description. AL6005-T5 Aluminum Alloy Solar PV Module Mounting Rack Rail. Solar Mounting Rails adopt aluminium oxide, Matched solar mounting rails can insert the proximate matter, Mounting rails with advanced technology which made the proximate matter and fastener easy to work come true.
How strong is 6060 aluminum?
Ultimate tensile strength: 140 to 230 MPa, or 20 to 33 ksi. Yield strength: 70 to 180 MPa, or 10 to 26 ksi. Thermal Expansion: 23.4 μm/m-K. Solidus: 610 °C or 1130 °F.
Can AlSi10Mg be anodized?
Until now, the colour grey-brown has dominated metal 3D printing, because components made of the primarily related standard alloy AlSi10Mg cannot be anodised well due to its silicon content of 9 to 11 percent. …
Where is AlSi10Mg used?
AlSi10Mg alloy is widely used in aviation, aerospace, automotive, machinery manufacturing, shipbuilding, chemical and other industrial fields [1,2].
Can 3D printed Aluminum be anodized?
Anodizing 3D-printed aluminum is technically possible but is limited because of the high percentage of silicium (10%) in the alloy (AlSi10Mg). A non-printed Aluminum part can be anodized more easily.
What is 6005A aluminium alloy?
Aluminium alloy 6005A is a medium strength, heat treatable alloy with excellent corrosion resistance. Alloy 6005 has properties between those of alloys 6061 and 6082 and can sometimes be used interchangeably with these alloys, but 6005 has better extrusion characteristics and a better mill surface finish.
What is the difference between 6005A and 6005 and 6061?
6005A displays improved toughness characteristics when compared to Alloy 6005 and Alloy 6105, and due to its chemical composition, 6005A provides improved extrudability compared to alloy 6061. However, because of the difference in manganese & chromium, alloy 6005A should not be confused with 6005.
What is the difference between 6082 and 6005 alloys?
Alloy 6005 has properties between those of alloys 6061 and 6082 and can sometimes be used interchangeably with these alloys, but 6005 has better extrusion characteristics and a better mill surface finish. It is difficult to produce thin-wall or complicated extrusions in 6005, but it is still more extrudable than 6082.
What is the ASTM code for 6005A?
6005A T1, T5, & T61 tempers are included in ASTM B221, ASTM B241, and ASTM B429 specifications. COMMON USES FOR ALLOY 6005A